Abbreviation
|
Result
|
Type
|
China Stander
|
Solvent
|
Capillary type
|
TEMP（℃）
|
Washing solvent
|
Foreign standards
|
PET
|
Intrinsic viscosity
|
聚对苯二甲酸乙二醇酯
Polyethylene terephthalate
|
GB 17931-03
GB/T14190-08
GB/T 1632.5-08
|
phenol tetrachloroethane(3:2)0.88
phenol tetrachloroethane(1:1)0.84
|
Ⅰc：0.84
|
25
|
Chloroform、Acetone
|
ISO 1628-5
ASTM D 4603
|
PBT
|
Intrinsic viscosity
|
聚对苯二甲酸丁二醇酯
英文名polybutylene terephthalate
|
FZ/T51005-11
|
phenol tetrachloroethane(3:2)0.88
|
Ⅰc
|
25
|
Acetone
|
ISO 1628-5
DIN 53727/3
|
PA
|
Intrinsic viscosity
|
聚酰胺（尼龙）
Polyamide/Nylon
|
GB/T12006.1-09
|
Sulfuric acid（96%）
|
Ⅱ:1.13
|
25
|
Sulfuric acid
|
ISO 307
|
Formic acid（90%）
|
Ⅰ:0.63
|
25
|
甲酸（90%）
|
ISO 307
ASTM D 789
| ||||
m-Cresol
|
Ⅱ:1.13
|
25
|
Dichloromethane
|
DIN 53727
ISO 307
| ||||
PAM
|
Intrinsic viscosity->molecular weight
|
聚丙烯酰胺(水处理剂)Poly(acrylamide)
|
GBT12005.1
|
Sodium chloride
|
4-0.55
4-0.57
|
30
|
铬酸洗液，水
| |
PC
|
Viscosity（reduced viscosity）
|
聚碳酸酯
Polycarbonate
|
HG/T 2234-91
|
Dichloromethane
|
0c:0.47
|
25
|
Dichloromethane
|
ISO 1628-4
|
PVC
|
Viscosity（reduced viscosity）、constant value
|
聚氯乙烯
Polyvinyl chloride
|
GB/T 3401-07
|
环已酮
|
Ⅰ:0.63
Ⅰc :0.84
|
25
|
Acetone
|
ISO 1628-2
ASTM D1243
|
TP
|
Viscosity（reduced viscosity）
|
热塑性均聚和共聚型聚酯
Thermoplastic polyester(TP) homopolymers and copolymers
|
GB/T1632.5
|
phenol tetrachloroethane(3:2)
|
Ⅰc :0.84
|
25
|
Acetone
|
ISO 1628-5
|
PCT
|
Viscosity（reduced viscosity）
|
聚对苯二甲酸环乙烯二亚甲基醇脂
|
GB/T1632.5
|
phenol tetrachloroethane(3:2)
|
Ⅰc:0.84
|
25
|
Acetone
|
ISO 1628-5
|
PEN
|
Viscosity（reduced viscosity）
|
聚萘二甲酸乙二醇酯
polyet hy2 lene nap ht halate
|
GB/T1632.5
|
phenol tetrachloroethane(3:2)
苯酚/三氯苯酚(3:2)
|
Ⅰc:0.84
|
25
|
Acetone
|
ISO 1628-5
|
URU
|
Viscosity/Intrinsic viscosity
|
聚氯醚树脂
Poly vinyl chloride resin
|
HG/T3605
|
环已酮：亚甲基酸(250:1)
|
3-0.59
|
50
|
环已酮
| |
POM
|
Viscosity/Intrinsic viscosity
|
聚甲醛树脂
Polyformaldehyde/acetaln resins
|
HG/T3604
|
对氯苯酚：α-蒎烯(98:2)
|
3-0.71
|
60
|
对氯苯酚
| |
Viscosity（reduced viscosity）
|
聚对苯二甲酸烷撑二脂
|
HG/T2364
|
苯酚：二氯苯(1:1)
间甲酚
|
Ⅰc:0.84
Ⅱ:1.13
|
25
|
铬酸溶液
|
ISO 1628-5
| |
PAN
|
Intrinsic viscosity
|
聚丙烯腈
Polyacrylonitrile
|
氯化锂\Dimethylformamide溶剂
|
Ic:0.84
|
25
|
Dimethylformamide，Acetone
| ||
PMMA
|
聚甲基丙烯酸甲酯
Polymethylmethacrylate
|
HG/T2626-94
HG/T2627-94
|
三氯甲烷
|
0c:0.47
Ⅰ:0.63
|
25
|
Acetone
Chloroform
|
ISO 1628/6
| |
PP
|
Viscosity（reduced viscosity）
|
聚丙烯
polypropylene
|
GB/T 1632.3-10
|
decahydronaphthalene(加稳定剂)
|
0b
0a:0.53
|
135
|
decahydronaphthalene(工艺级)
|
DIN 53728/4
ISO 1191
|
PE
|
Viscosity（reduced viscosity）
|
聚乙烯
polyethylene
|
GB/T 1632.3-10
|
decahydronaphthalene(加稳定剂)
|
0b
0a:0.53
|
135
|
decahydronaphthalene(工艺级)
|
ISO 1628-3
ASTMD1601
|
PS
|
Intrinsic viscosity
|
聚苯乙烯
Polystyrene
|
Toluene
|
Ⅰ:0.63
|
25
|
Toluene、Acetone
| ||
PIB
|
聚异丁烯
Polyisobutylene
|
Dimethylformamide
|
Ⅰc :0.84
|
25
|
Dimethylformamide，Acetone
| |||
PSU
|
聚砜
polysulfone
|
N-Methyl-2-pyrrolidone
|
Ⅰc :0.84
|
25
|
N-Methyl-2-pyrrolidone
Acetone
| |||
PLA
|
聚乳酸酯
Polylactic Acid/
Polylactide
|
Chloroform
|
0c:0.47
|
25
|
Chloroform、Acetone
| |||
SAN
|
苯乙烯/丙烯腈共聚物
acrylonitrile-styrene copolymer
|
Dimethylformamide
|
Ⅰc:0.84
|
25
|
Dimethylformamide
Acetone
| |||
SB
|
苯乙烯/丁二烯共聚物
Styrene/butadiene copolymer
|
Toluene
|
0c:0.47
Ⅰ:0.63
|
25
|
Toluene、Acetone
| |||
TPU
|
热塑塑料聚氨基甲酸乙酯/聚氨酯Ethyl carbamate
Polyurethane/
|
Dimethylformamide
|
Ⅰc:0.84
|
25
|
Dimethylformamide
Acetone
| |||
PU
|
聚氨酯(聚氨基甲酸酯)
polyurethane
|
Dimethylformamide
| ||||||
CA
|
Viscosity、viscosity ratio
|
乙醋纤维素
|
HG/T 2758
|
Dichloromethane Methanol solvent
|
M1
|
25
|
ISO 1157
| |
Chitin
|
Intrinsic viscosity->Averagemolecular weight
|
甲壳素
Chitin
|
SC/T 3403
ChemicalBookⅥG
|
Acetic acid
|
25
30
|
Distilled water
| ||
MCC
|
Intrinsic viscosity->Averagemolecular weight
|
微晶纤维素
AVICEL PH;AVICEL PH 101(R) |
ChemicalBookⅥG
|
CUPRIETHYLENEDIAMINE
|
Oc:0.47
Ic:0.84
|
10%Acetic acid
|
BASF
| |
Intrinsic viscosity->Averagemolecular weight
|
羟丙甲纤维素
Hypromellose
|
ChemicalBookⅥG
|
Distilled water
|
Oa:0.53
| ||||
kinematic viscosity
|
硅油类
Polydimethylsiloxane
|
根据粘度范围
|
Methanol60-90
| |||||
Specific viscosity->Polymerization Degree
|
浆柏\棉纤维
Pulp \ cotton fiber
|
GB/T9107(0.80)
|
铜氨溶液
|
Ⅰ:0.63
|
25
|
10%Acetic acid
| ||
limit viscosity
|
水处理剂
Water treatment agent
|
GB/T22593-2008
|
Oa:0.53
|
30
| ||||
Intrinsic viscosity(马丁法)
|
粘胶纤维用浆粕(棉/木/竹/麻浆粕)
Pulps for viscose fibres (cotton / Wood / bamboo / hemp pulp)
|
FZ/T
50010.3-1998
|
20
|
ISO 5351/1
| ||||
relative viscosity->Intrinsic viscosity->Polymerization Degree
|
兰麻 纤维素
Bast fiber
|
GB 5888-86
|
铜乙二胺溶液
bis(1,2-ethanediamine-n,n')-copper(dihydroxide)
|
奥式0.5 0.6
|
25
|
10%Acetic acid
|
Polymerization Degree
| |
PVAL
|
AveragePolymerization Degree
|
聚乙烯醇树脂
polyvinyl alcohol
|
GB 12010.5
|
Distilled water
Distilled water
|
奥 0.6
|
30
|
Polymerization Degree
| |
AveragePolymerization Degree
|
聚乙烯醇
polyvinyl alcohol,vinylalcohol polymer
|
GB 12010.5
|
Distilled water
Distilled water
|
奥 0.6
| ||||
PPS
|
250
| |||||||
| |
| |
|